Variable pitch IC bond pad arrangement

ABSTRACT

The bond pads (22) for a ceramic package (10) are deposited on the pre-fired ceramic with the bond pad widths (47) increasing as a function of the distance (49) of each pad from the center of package mass (40), whereby bond pads at the extremity (36) of the package have the largest pad width and pads toward the center (40) of the package have the narrowest width.

DESCRIPTION

1. Technical Field

This invention relates to integrated circuit (IC) packaging, and more particularly to ceramic IC packages.

2. Background Art

The manufacture of ceramic microelectronic packages by the co-firing process involves deposition of trace refractory metallization on the unfired, or "green" tape cast of the ceramic IC carrier. The trace metal represents the package bond pads which the IC die leads attach to. The firing of the green tape shrinks the ceramic to a final, post-fired size. The shrinkage is predictable (on the order of 18%) to within a +/- "acceptable variation" tolerance. The standard variation tolerance is +/-1.0% of the nominal post-fired ceramic body dimension.

The trace metal also shrinks predictably when the ceramic is fired, with the same +/-1.0% variation tolerance on size and geometrical spacing. If a first array of trace line metal is deposited on the green tape ceramic and is intended for post-fired registration with a second array of trace metal having a nominal dimension of 1.0 inches, then the final dimension of the first array may be 1.000+/-0.010 inches.

Prior art methods of mounting the IC dies to the ceramic package bond pads include both manual and automated bonding processes. In the manual processes the electrical interconnection of the IC to the package require operator alignment of the IC interconnect wires (or ribbon) to the bond pads. After alignment a bonder machine secures the device leads to the bond pads by welding or soldering. Automated processes, such as tape automated bonding (TAB), require accurate positioning of the package bond pads so as to automatically receive the IC TAB leads in register. The +/-1.0% shrinkage tolerance creates problems with the TAB to bond pad registration.

While the bond pads may be made large enough to accommodate all manufacturing tolerances, including the shrinkage tolerance, this prevents increasing package density. The IC industry drive towards miniaturization requires high density packaging which prohibits this brute force method of lead registration.

DISCLOSURE OF INVENTION

The object of the present invention is to provide a method of designing the widths of the bond pad trace metallization deposited on a pre-fired ceramic package so as to ensure automatic post-fired registration of the package bond pads with the IC device TAB leads.

According to the present invention, the bond pad metallization for a ceramic package is deposited on the pre-fired ceramic with the bond pads widths increasing as a function of the distance of each pad from the center of package mass toward which the ceramic shinkage takes place, whereby bond pads at the extremity of the package have the largest pad width and pads toward the center of the package have the narrowest width.

With the present invention, the widths of the package bond pads which are furthest from the center of package mass are made wider than those pads closest to the center. The greater the distance from the center of mass, the greater the effect of the feature displacement due to the +/-1.0% tolerance. Since the furthest bond pads experience the greatest shrinkage tolerance variation, and resultant feature displacement, increasing their width ensures their registration with the IC TAB leads under the worst case conditions of the post-fired tolerance. Similarly the bond pads closest to the center of package mass are deposited with the smallest widths. Since the closer pads experience the minimum shrinkage tolerance variation, and resultant minimum feature displacement, the narrower widths still ensure registration with the IC leads. Instead of making all of the bond pads uniformly wide the actual width of each pad varies with the pad's location from the package center of mass.

The present invention takes advantage of the fact that ceramic shrinkage with firing is not constant across the ceramic body. Instead, the different areas of the ceramic body shrink by a percentage dependent on the distance of the area from the center of mass. The amount of shinkage is greater at the periphery, and decreases from the outer edges towards the center of the body in a more or less predetermined fashion, subject to the +/-1.0% tolerance.

These and other objects, features, and advantages of the present invention will become more apparent in light of the following detailed description of a best mode embodiment thereof, as illustrated in the accompanying drawing.

BRIEF DESCRIPTION OF THE DRAWING

FIG. 1 is a topographical plan view of a ceramic package in which the present invention may be used;

FIG. 2 is a perspective illustration of the mounting relationship between an IC device and the ceramic package of FIG. 1; and

FIG. 3 is an illustration of a portion of an array of bond pad metallization deposited by the method of the present invention on the ceramic package of FIG. 1.

BEST MODE FOR CARRYING OUT THE INVENTION

FIG. 2 illustrates a standard, leadless ceramic package (chip carrier) 10 in which the present invention may be used. The package includes a substrate 11, having a symmetrical central cavity 12. The cavity is stepped, to provide a bond shelf 13 having an outer dimension Dc and an inner dimension D_(d). The Dd dimension is larger than that of a silicon IC die 14 to be mounted in the package. The die is mounted to a tape 16 using a tape automated bonding (TAB) process known in the art. The tape connects the die terminals to input/output (I/O) TAB leads 18. The TAB leads have a lead width (T_(w)) 20.

The tape-mounted die is fitted into the lower part of the cavity, with registration of the IC TAB leads 18 to the package bond pads 22 arrayed along the bond pad shelf 13; on all four sides of the cavity 12. The TAB leads are welded, or soldered to the package bond pads. The bond pads 22 are connected (not shown) through the substrate 11 to corresponding outer bond pads 26, which allow connection of the IC to user equipment outside the package.

The IC TAB process, the fabrication of the ceramic package, the deposition of the bond pad metallization, and the mounting of the IC to the package, are all accomplished through known, prior art methods. The bond pads may be deposited using any one of a number of known deposition techniques, i.e. photolithographic deposition. They are not a part of the present invention. The present invention relates to the method of calculating the finished post-fired pad width (PAD₋₋ W) of each of the shelf bond pads 22 so that in the post-fired ceramic each of the bond pads provide sufficient pad surface contact in register with the TAB leads to allow automated bonding. The method takes advantage of the ceramic shrinkage characteristic where the ceramic furthest from the package center of mass shrinks with the most variation, with shrinkage decreasing toward the center.

FIG. 1 is a plan view of the ceramic package 10 of FIG. 2. Bond pad metallization is deposited on all four sides of the cavity shelf 13. In the present invention, the bond pads are deposited such that the PAD₋₋ W values of the pads disposed closest to centers (X) 28-31 of each side 32-35 have a minimum width, and the pads at the extreme corners 36-39 of each side have a maximum width. The sides are symmetrical about the center of mass 40 of the ceramic carrier. The centers 28-31 are also the center of symmetry of the sides about the center of mass, as shown by the orthogonal X axes eminating from the center. The X axes divide the package surface into four quadrants 42-45.

The length of the bond pad array on each side is specified by a bond pad centerline spread feature size F for each side, as illustrated for the side 32. The PAD₋₋ W widths of the pads over the feature size F are symetrical about the centers (X) 28-31 of each side. Therefore, the variation of PAD₋₋ W from minimum to maximum occurs over one half the feature size (F/2). By determining the PAD₋₋ W pattern over the length F/2 for a one half segment of a side (e.g., the segment 46 of side 32), the pad pattern may be replicated eight times.

FIG. 3 illustrates the quadrant 42 with the segment 46 of side 32. The embodiment of the present method is described with respect to a ceramic package having a total of 144 bond pads. There are 36 pads per side, with 18 pads for each F/2 segment. As shown for segment 46 the pads are numbered from #1 at the corner 36 to #18 at the center 28.

There are three parameters which must be calculated for each of the pads in the F/2 segment array. These include: the pad width (PAD₋₋ W(i)) 47 (where (i) is from 1 to 18), which is the edge-to-edge dimension of each pad; the pad pitch (PAD₋₋ PP(i)) 48, which is the center-to-center dimension of each pad; and the pad coordinate (PAD₋₋ X(i)) 49, which is the distance of a pad centerline from the (e.g., 50) to the side centerline 28.

The parameter PAD₋₋ G 52 is the minimum gap (edge-to-edge spacing of adjacent pads) dimension, and is essentially constant over the feature spread F. As known to those skilled in the art, there are various other manufacturing parameters which must be specified for the bond pads, but which are not shown in FIG. 3 to avoid confusion in the illustration. Such of these parameters as are necessary to the present method are described in Appendix A.

The PAD₋₋ W(i) and PAD₋₋ PP(i) values are directly related to: the manufacturing tolerances (MT) associated with the TAB lead-to-bond pad alignment, and the value of the spread feature size (F) and its (the ceramic package) standard variation shrinkage tolerance (PKG₋₋ SHR) (e.g., +/-1.0% F). The MT parameters include:

TAB lead width (TAB₋₋ W),

TAB lead width tolerance (TAB₋₋ WT),

TAB lead positional tolerance (TAB₋₋ PT),

TAB lead-to-bond pad alignment tolerance (TAB₋₋ AT),

bond pad positional tolerance (PAD₋₋ PT),

bond pad width tolerance (PAD₋₋ WT), and

TAB lead overhang (TAB₋₋ OH) from the bond pad edge, expressed as a percent of TAB lead width.

The MT values are discussed in detail with respect to Appendix A.

Referring to Appendix A, Equation (1) defines the PAD₋₋ W(i) values in terms of the MT parameters, and the shrinkage variation tolerance. The TAB₋₋ AT, TAB₋₋ PT, PAD₋₋ PT and TAB₋₋ W*TAB₋₋ OH parameters are a +/- tolerance. Equation (1) treats the worst case requirements of PAD₋₋ W(i) by taking the absolute worst case of each +/- tolerance (i.e. 2x). The MT factor is a constant for a given package configuration.

The shrinkage tolerance factor, however, varies with pad placement; it varies as a function of PAD₋₋ X(i). Since PAD₋₋ X(i) (49, FIG. 3) is the distance of each pad centerline (50) from the center of symmetry, i.e. centerline (28, FIG. 3) of the bond pad shelf, PAD₋₋ X(i) is a minimum for the first pad from the centerline (note: if there are an odd number of bond pads per package side, the two half spread feature (F/2) regions will share the center pin, i.e. PAD₋₋ W(1)/2, and PAD₋₋ X(1)=0) the shrinkage tolerance for PAD₋₋ W(1) is zero, or near zero. PAD₋₋ W(1) then is essentially equal to MT. The shrinkage tolerance of the PAD₋₋ W(N) value at the feature spread extremity is obviously maximum.

Equation (2) defines PAD₋₋ X(i) as the sum of: 1/2 the present and preceding pad widths, the gap dimension (PAD₋₋ G), and the previous pad PAD₋₋ X(i) value. Equation (3) defines the PAD₋₋ PP value (48, FIG. 3) as the difference value between successive PAD₋₋ X(i) values. Equation (4) is obtained by substituting the term MT for the manufacturing tolerances, the Equation (2) for PAD₋₋ X(i) into Equation (1).

It should be noted that PAD₋₋ W(i), PAD₋₋ PP(i), and PAD₋₋ X(i) are the respective post-fired values for the pad widths, pad pitches, and pad coordinates. In order for the manufacturer to determine the corresponding pre-fired, or "green", values, the PAD₋₋ W(i), PAD₋₋ PP(i), and PAD₋₋ X(i) values must be magnified by the ceramic shrinkage value that the manufacturer anticipates. In the example of an 18% expected firing shrinkage, PAD₋₋ W(i), PAD₋₋ PP(i), and PAD₋₋ X(i) would be divided by the quantity (1.00-0.18)=0.82, to obtain the pre-fired values.

Appendix A, Sheet 2, lists the MT parameter values for an exemplary calculation of bond pad widths for a ceramic package having 144 pads (TAB₋₋ IO=144); an even number of pads per side (PKG₋₋ SYM=EVEN). This is 36 pads per full feature spread (F), or 18 pads per F/2 (PAD₋₋ N=18). As shown, the PAD₋₋ PP, PAD₋₋ W, and PAD₋₋ X values are variable, and determined by Equations (3), (4), and (2) respectively. Sheet 3 of Appendix X lists their calculated values. The pad closest the side centerline is listed as "18"; the extreme pad is "1".

As shown, the PAD₋₋ W values are only calculated for one half the total number of pads to be disposed on each side. The calculated array is then replicated for the remaining half of the side, and for each other half side on which pads are to be disposed. It should be understood that the present method may be used to determine the PAD₋₋ W values of bond pads disposed in any surface area of the ceramic carier; it is not limited to use on the carrier sides alone.

Similarly, although the invention has been shown and described with respect to a best mode embodiment thereof, it should be understood by those skilled in the art that various other changes, omissions, and additions may be made therein without departing from the spirit and scope of the invention.

                                      APPENDIX A                                   __________________________________________________________________________     BOND PAD WIDTH                                                                  (1)                                                                              ##STR1##                                                                      .BHorizBrace.                                                                  MANUFACTURING TOLERANCES (MT) = CONSTANT                                       2*0.01*PKG --SHR*PAD --X(i)                                                  WHERE:     TAB --AT                                                                             TAB lead to package lead assembly alignment tolerance                    TAB --OH                                                                             Maximum TAB lead overhang from the package                                     bond pad edge, in percent of TAB lead width                              TAB --PT                                                                             TAB lead positional tolerance                                            TAB --W                                                                              Nominal TAB lead width                                                   TAB --WT                                                                             TAB lead width tolerance                                                 PAD --PT                                                                             Package bond pad positional tolerance                                    PAD --WT                                                                             Package bond pad width tolerance                                         PAD --X                                                                              Bond pad and TAB OLD coordinate from centerline                          PKG  --SHR                                                                           Firing shrinkage tolerance of ceramic package(%)              (2)                                                                              PAD --X(i) = PAD --X(i - 1) + 0.5*PAD --W(i - 1) + PAD --G + 0.5*PAD           --W(i)                                                                       WHERE:     PAD --G                                                                              Nominal package bond pads gaps                                (3)                                                                              PAD --PP = PAD --X(i) - PAD --X(i - 1)  Bond pad pitch, from the               previous bond pad                                                              SUBSTITUTING(MT) and EQ(2) INTO EQ(1), and simplifying                        (4)                                                                              ##STR2##                                                                    __________________________________________________________________________     FOLLOWING IS AN EXAMPLE OF CALCULATING THE BOND PAD WIDTHS USING EQ(4),        TOGETHER WITH THE                                                              BOND PAD COORDINATE AND BOND PAD PITCH USING EQS(2), (3), FOR A 144 BOND       PAD PACKAGE HAVING                                                             THE FOLLOWING PARAMETERS.                                                      TAB OLD AND PACKAGE PARAMETERS (SPECIFIED):                                    TAB PARAMETERS (SPECIFIED)                                                     TAB --IO          Total number TAB leads and internal package bond                                                               144s                         TAB --AT          TAB lead to package lead assembly alignment                                                                    0.0002nce                    TAB --OH          Maximum TAB lead overhang from the package                                                                     25.0000%                                       bond pad edge, in percent of TAB lead width                  TAB --PT          TAB lead positional tolerance   0.0002                       TAB --W           Nominal TAB lead width          0.0040                       TAB --WT          TAB lead width tolerance        0.0002                       PACKAGE INTERNAL BOND PAD PARAMETERS (SPECIFIED):                              PAD --G           Nominal package bond pads gaps  0.0058                       PAD --PT          Package bond pad positional tolerance                                                                          0.0005                       PAD --WT          Package bond pad width tolerance                                                                               0.0010                       PACKAGE BOND PAD PATTERN PARAMETERS (CALCULATED):                              PAD --N           Integer number of package bond pads                                                                            18                                             per 1/2 bond shelf width                                     PAD --PP          Bond pad pitch, from the previous bond                                                                         variable                     PAD --W           Bond pad width                  variable                     PAD --X           Bond pad and TAB OLD coordinate from centerline                                                                variable                     PKG --SYM         Bond pad row symetry, even and odd                                                                             EVEN                         __________________________________________________________________________     THE CALCULATED PAD --W, PAD --PP, AND PAD --X ARE LISTED BELOW FOR ONE         HALF OF ONE SIDE OF THE                                                        PACKAGE (1/8TH OF 144 PIN TOTAL). THE BOND PAD PATTERN IS REPLICATED           EIGHT TIMES.                                                                   (FIRED) PACKAGE OUTER LEAD BONDS PADS (8 FOLD SYMMETRY)                        FOR TAB APPLICATIONS                                                                       PAD --W             PAD --PP                                                                               PAD --X                                            WIDTH               PITCH (REF)                                                                            COORDINATE                                    (pad #)                                                                             (inches)            (inches)                                                                               (inches)                               __________________________________________________________________________            18   0.0051              0.0054  0.0054                                        17   0.0053              0.0110  0.0164                                        16   0.0056              0.0112  0.0276                                        15   0.0058              0.0114  0.0390                                        14   0.0060              0.0116  0.0506                                        13   0.0063              0.0119  0.0625                                        12   0.0065              0.0121  0.0747                                        11   0.0067              0.0124  0.0870                                        10   0.0070              0.0126  0.0996                                        9    0.0073              0.0129  0.1125                                        8    0.0075              0.0131  0.1256                                        7    0.0078              0.0134  0.1390                                        6    0.0081              0.0137  0.1527                                        5    0.0083              0.0139  0.1666                                        4    0.0086              0.0142  0.1809                                        3    0.0089              0.0145  0.1954                                        2    0.0092              0.0148  0.2102                                        1    0.0095              0.0151  0.2253                                 __________________________________________________________________________ 

I claim:
 1. The method of disposing metal bond pads on the surface of a pre-fired ceramic substrate having a shrinkage tolerance, to provide registration of the bond pads with the leads of an integrated circuit (IC) die mounted to the post-fired substrate by automated process, comprising the steps of:locating, with respect to the substrate center of mass, the center of symmetry of a length of surface area in which the bond pads are to be disposed; marking half length regions equal to one half said length on each side of said center of symmetry; and disposing one half the bond pads in each said half length region in substantially identical arrays, each array characterized by the pads being disposed at different bond pad widths which increase from a minimum value for a bond pad disposed adjacent said center of symmetry to a maximum value for the pad disposed furthest from said center of symmetry.
 2. The method of claim 1, wherein said step of disposing includes the step of depositing the bond pads with substantially equal spacing between adjacent edges of adjacent pads.
 3. The method of claim 1, wherein each bond pad width includes the sum of a manufacturing tolerance and a ceramic shrinkage tolerance, said manufacturing tolerance being constant for each bond pad, said ceramic shrinkage tolerance increasing from a minimum value for a bond pad disposed adjacent to said center of symmetry to a maximum value for the bond pad disposed furthest from said center of symmetry.
 4. The method of claim 3, wherein said step of disposing each said array includes the steps of:applying the bond pad adjacent to said center of symmetry at a pad width substantially equal to said manufacturing tolerance value; measuring the coordinate distance value from said center of symmetry to the centerline of said adjacent pad; depositing a next succeeding bond pad spaced from a preceding bond pad by a gap value, at a pad width substantially equal to the sum of said manufacturing tolerance value and the product of said coordinate distance value multiplied by twice the absolute value of the ceramic shrinkage tolerance value; determining the coordinate distance value from said preceding bond pad centerline to said next succeeding bond pad centerline and adding this to the sum total of all preceding coordinate distance values; and continuing said step of depositing and said step of determining up to the applying of said bond pad furthest from said center of symmetry. 